Did you know that a complete removal of temporary cement from the abutment tooth with a rubber cup and pumice paste or an ultrasonic scaler is usually impossible? In most cases, some visibly undetectable residues remain on the surface. They will negatively affect the bonding performance of the permanent cementation system you selected. KATANA™ Cleaner is our answer to this problem! Applied after conventional temporary cement removal, it provides optimal conditions for permanent cementation.

All relevant details are revealed in this scientific report.

Did you know that a complete removal of temporary cement from the abutment tooth with a rubber cup and pumice paste or an ultrasonic scaler is usually impossible? In most cases, some visibly undetectable residues remain on the surface. They will negatively affect the bonding performance of the permanent cementation system you selected. KATANA™ Cleaner is our answer to this problem! Applied after conventional temporary cement removal, it provides optimal conditions for permanent cementation.

All relevant details are revealed in this scientific report.

By Aleksandra Łyżwińska, DMD

The MOD restoration on the maxillary left second premolar of this patient was in need of replacement. It was decided to create a direct composite overlay with CLEARFIL MAJESTY™ ES Flow - Super Low A3, CLEARFIL MAJESTY™ ES-2 Classic A2. CLEARFIL™ SE BOND 2 was used after selective etching of the enamel to establish a chemical bond to enamel and dentin. For the finishing and polishing procedure, abrasive discs were used first, followed by silicon carbide rubber instruments and the CLEARFIL™ Twist DIA system.

Fig. 1. Initial clinical situation revealing the composite restoration to be replaced on the second premolar.

Fig. 2. Occlusal view of the teeth after cavity preparation including cusp reduction.

Fig. 3. Lateral view of the teeth after cavity preparation.

Fig. 4. Matrix band held in place with wedges and two rings.

Fig. 5. Situation after etching, bonding, removal of one ring, and build-up of the interproximal walls with CLEARFIL MAJESTY™ ES-2 Classic in the shade A2.

Fig. 6. Cavity filled with CLEARFIL MAJESTY™ ES Flow - Super Low A3.

Fig. 7. Occlusal surface restored with CLEARFIL MAJESTY™ ES-2 Classic in the shade A2.

Fig. 8. Polishing with the pre-polisher of the CLEARFIL™ Twist DIA system.

Fig. 9. Polishing with the high-shine polisher of the CLEARFIL™ Twist DIA system.

Fig. 10. Appearance of the restoration immediately after rubber dam removal and checking of the occlusal contacts.

FINAL SITUATION

Fig. 11. Linguo-occlusal view of the treatment outcome.

Fig. 12. Lateral view of the treatment outcome.

Dentist:

ALEKSANDRA ŁYŻWIŃSKA
Warsaw, Poland

Aleksandra Łyżwińska, DMD, is a passionate aesthetic and adhesive dentist. Driven by Evidence Based Dentistry, her goal includes using modern composite materials and bonding agents in her clinical practise. In addition to her primary job, she worked as a lecturer and an assistant professor at the Department of Conservative Dentistry and Endodontics of Medical University of Warsaw, her alma mater.

By Aleksandra Łyżwińska, DMD

The MOD restoration on the maxillary left second premolar of this patient was in need of replacement. It was decided to create a direct composite overlay with CLEARFIL MAJESTY™ ES Flow - Super Low A3, CLEARFIL MAJESTY™ ES-2 Classic A2. CLEARFIL™ SE BOND 2 was used after selective etching of the enamel to establish a chemical bond to enamel and dentin. For the finishing and polishing procedure, abrasive discs were used first, followed by silicon carbide rubber instruments and the CLEARFIL™ Twist DIA system.

Fig. 1. Initial clinical situation revealing the composite restoration to be replaced on the second premolar.

Fig. 2. Occlusal view of the teeth after cavity preparation including cusp reduction.

Fig. 3. Lateral view of the teeth after cavity preparation.

Fig. 4. Matrix band held in place with wedges and two rings.

Fig. 5. Situation after etching, bonding, removal of one ring, and build-up of the interproximal walls with CLEARFIL MAJESTY™ ES-2 Classic in the shade A2.

Fig. 6. Cavity filled with CLEARFIL MAJESTY™ ES Flow - Super Low A3.

Fig. 7. Occlusal surface restored with CLEARFIL MAJESTY™ ES-2 Classic in the shade A2.

Fig. 8. Polishing with the pre-polisher of the CLEARFIL™ Twist DIA system.

Fig. 9. Polishing with the high-shine polisher of the CLEARFIL™ Twist DIA system.

Fig. 10. Appearance of the restoration immediately after rubber dam removal and checking of the occlusal contacts.

FINAL SITUATION

Fig. 11. Linguo-occlusal view of the treatment outcome.

Fig. 12. Lateral view of the treatment outcome.

Dentist:

ALEKSANDRA ŁYŻWIŃSKA
Warsaw, Poland

Aleksandra Łyżwińska, DMD, is a passionate aesthetic and adhesive dentist. Driven by Evidence Based Dentistry, her goal includes using modern composite materials and bonding agents in her clinical practise. In addition to her primary job, she worked as a lecturer and an assistant professor at the Department of Conservative Dentistry and Endodontics of Medical University of Warsaw, her alma mater.

Universal applicability of dental materials – this is a feature highly valued by the products’ users. It allows them to slim down the range of materials needed, which leads to reduced stock inventory and facilitates the establishment of universal workflows. With fewer variables and inconsistencies, all members of the practice team will know exactly what to do and how to do it, which mean less errors and consistent outcomes.

As one of the leading developers and providers of bonding agents, cements and composite filling as well as indirect restorative materials, Kuraray Noritake Dental strongly supports the universality trend in dentistry. Popular examples of universal products for direct restoration procedures are CLEARFIL™ Universal Bond Quick, a one-step dental bonding agent that works with or without a separate etching step, and the filling material CLEARFIL MAJESTY™ ES Flow.

Indirect restorative workflows are streamlined e.g. with PANAVIA™ SA Cement Universal, a self-adhesive resin cement indicated for all kinds of restorative materials, which is always used according to the same universal protocol.

Prior to the use of this product, the dental practitioner should consider cleaning the tooth and the restoration with KATANA™ Cleaner indicated for extra- and intra-oral use and providing optimal conditions for a strong and durable bond.

Both products recently received very positive ratings from the evaluators of Clinician’s Report. Click here to see the evaluations!

Universal applicability of dental materials – this is a feature highly valued by the products’ users. It allows them to slim down the range of materials needed, which leads to reduced stock inventory and facilitates the establishment of universal workflows. With fewer variables and inconsistencies, all members of the practice team will know exactly what to do and how to do it, which mean less errors and consistent outcomes.

As one of the leading developers and providers of bonding agents, cements and composite filling as well as indirect restorative materials, Kuraray Noritake Dental strongly supports the universality trend in dentistry. Popular examples of universal products for direct restoration procedures are CLEARFIL™ Universal Bond Quick, a one-step dental bonding agent that works with or without a separate etching step, and the filling material CLEARFIL MAJESTY™ ES Flow.

Indirect restorative workflows are streamlined e.g. with PANAVIA™ SA Cement Universal, a self-adhesive resin cement indicated for all kinds of restorative materials, which is always used according to the same universal protocol.

Prior to the use of this product, the dental practitioner should consider cleaning the tooth and the restoration with KATANA™ Cleaner indicated for extra- and intra-oral use and providing optimal conditions for a strong and durable bond.

Both products recently received very positive ratings from the evaluators of Clinician’s Report. Click here to see the evaluations!

By Dr. Michał Sucholdolski

This patient was concerned about the discoloration that had appeared on the occlusal surface of the mandibular left first molar. In an intraoral examination, caries was diagnosed in this area.

As the occlusal surface was almost intact initially, it was decided to restore the tooth with resin composite using the stamp technique. For this purpose, the occlusal anatomy was recorded using CLEARFIL MAJESTY™ ES Flow in the shade A3, which was stamped onto the occlusal surface and fixed to an applicator by light curing. Afterwards, the carious tissue was removed with the aid of caries-detector dye. Following cleaning of the prepared cavity and application of the bonding agent (CLEARFIL™ SE BOND 2), CLEARFIL MAJESTY™ ES Flow (A3) was applied to the cavity floor. The final occlusal layer was created with CLEARFIL MAJESTY™ ES-2 in the shade A3. The stamp was used to transfer the original occlusal anatomy to the new surface before light curing. A natural gloss was obtained by polishing of the surface with the CLEARFIL™ Twist DIA system.

Fig. 1. Initial clinical situation with an occlusal surface affected by caries.

Fig. 2. Appearance of the tooth after the application of caries detector dye during cavity preparation.

Fig. 3. Stamp created with flowable resin composite.

FINAL SITUATION

Fig. 4. Treatment outcome.

Dentist:

Dr. Michał Sucholdolski is a graduate of Silesia Medical University in Zabrze, Poland. He has attended various national and international conferences on microscopic dentistry, endodontic treatment and aesthetic restorative dentistry.

He makes use of innovative dental approaches such as Digital Smile Design, the MicroVision preparation concept, minimally invasive preparation techniques and modern direct restoration techniques.

He is a Member of the Polish Association of Endodontic Treatment and author of scientific work and publications in dental magazine.

By Dr. Michał Sucholdolski

This patient was concerned about the discoloration that had appeared on the occlusal surface of the mandibular left first molar. In an intraoral examination, caries was diagnosed in this area.

As the occlusal surface was almost intact initially, it was decided to restore the tooth with resin composite using the stamp technique. For this purpose, the occlusal anatomy was recorded using CLEARFIL MAJESTY™ ES Flow in the shade A3, which was stamped onto the occlusal surface and fixed to an applicator by light curing. Afterwards, the carious tissue was removed with the aid of caries-detector dye. Following cleaning of the prepared cavity and application of the bonding agent (CLEARFIL™ SE BOND 2), CLEARFIL MAJESTY™ ES Flow (A3) was applied to the cavity floor. The final occlusal layer was created with CLEARFIL MAJESTY™ ES-2 in the shade A3. The stamp was used to transfer the original occlusal anatomy to the new surface before light curing. A natural gloss was obtained by polishing of the surface with the CLEARFIL™ Twist DIA system.

Fig. 1. Initial clinical situation with an occlusal surface affected by caries.

Fig. 2. Appearance of the tooth after the application of caries detector dye during cavity preparation.

Fig. 3. Stamp created with flowable resin composite.

FINAL SITUATION

Fig. 4. Treatment outcome.

Dentist:

Dr. Michał Sucholdolski is a graduate of Silesia Medical University in Zabrze, Poland. He has attended various national and international conferences on microscopic dentistry, endodontic treatment and aesthetic restorative dentistry.

He makes use of innovative dental approaches such as Digital Smile Design, the MicroVision preparation concept, minimally invasive preparation techniques and modern direct restoration techniques.

He is a Member of the Polish Association of Endodontic Treatment and author of scientific work and publications in dental magazine.

By Marco Stoppaccioli

In today´s society, due to higher life expectancy, greater and more responsible attention to one´s body, we have developed a culture more sensitive to personal well-being. Consequently, more patients with total removable prostheses request stabilization of their prostheses through implant treatment which offers the most effective and valid response to this need.

The demand for implant treatments has increased significantly during the last decade, specifically from patients with long-term full prostheses resulting in considerable bone resorption¹, but are hesitant to undergo complex bone regeneration interventions (Photo 1).

These rehabilitations require great commitment and professional skills. In addition to restoring a complex series of aesthetic-functional parameters that have been lost. Innovative products were developed, not only the restoration of the dental, but also, the orthopedic aspects of the procedure.

Photo 1: Upper and lower Jaw situation models.

Initially, the dental-skeletal rehabilitations involved the exclusive use of metal posts combined with acrylic materials.

In recent decades, we have witnessed an evolution in the surgical techniques and materials used, among these, zirconia² has a significant and highly innovative role. The main reason for its success is due to the possibility of being able to use it anatomically through a simple and effective protocol thanks to CAD CAM technology.

Zirconia, created to be covered with ceramic coatings, has undergone a profound evolution: from an exclusively structural material with high strength but low aesthetic appeal, it has become anatomical, constituting an alternative to layered restorations. Thanks to research and innovation, optimizing chemical and physical parameters³ in the dental industry, we now have a wide range of products, including multi-layer zirconia.

In more analytical terms, it offers a very valid response to the translucency, which is inversely proportional to the flexural strength. On the market this material class oscillates between 550Mpa and 1200Mpa of flexural strength. This characteristic identifies its indication range, specifically depending on the yttrium oxide content, which acts as a stabilizer of zirconia.

For dental-skeletal rehabilitations, the protocol involves the use of multi-layer monolithic zirconia with marked characteristics of flexural strength but lower translucency which determines a limit in the aesthetic sense. On the other hand, the use of multi-layered zirconia with high translucency cannot be considered suitable, due to its lack of flexural strength, despite fully meeting the requirement for naturalness.

To date it can be said that there is no zirconia that offers high mechanical properties combined with high translucency, two fundamental aspects for successful restorations.

Considering these factors, the idea was born to generate an innovative and experimental protocol capable of supporting, on the one hand, the ability of CAD/CAM systems to copy exactly a project or even better, a functionalized provisional implant, and on the other, to associate the use of two zirconia with different characteristics: one extremely tough, white colored zirconia with 1125 MPa (KATANA™ HT Kuraray Noritake) and the other super translucent multi-layered zirconia with 750 MPa (KATANA™ STML Kuraray Noritake).

OPERATIONAL PROTOCOL

In dental-skeletal rehabilitations, success depends on a precise diagnosis by the clinician, aimed at the functional and aesthetic restoration of the case. It is a fundamental task of the dental technician to translate this information through the creation of a wax-up, both analog and digital.

Photo 2: Digital wax-up.

Photo 3: Analog wax-up.

Thanks to digitization, with a 3D printer, it is possible to realize the wax-up quickly and economically in a prototype, capable of allowing the clinician to perform an initial test in the oral cavity.

Photo 4: From design to 3D prototype.

Once the adequacy of the prototype under study has been certified, the next phase involves the construction of the provisional implant which, placed in the oral cavity for a specified time, provides the fundamental information from an occlusal point of view, both in static and dynamic conditions.

The first strength of this protocol is to capture all information about the provisional implant and transfer them to the final work through digital systems. In other words, the provisional implant itself becomes the design of the final product.

Photo 5: Temporary result of analog project.

Photo 6: Acquisition of temporary arches refitted on the models.

FINAL PROCEDURE: OPERATING PHASES

Once the scans of the temporary implant have been acquired in the digital platform, the structural frame obtained by reduction of the temporary implant file is generated. The framework will be made by using KATANA™ HT white colored zirconia (Kuraray Noritake Dental Inc.) with a flexural strength of 1125 MPa. This choice is attributable to an adequate toughness of the material and an effective aesthetic chromatic response on the pink ceramic coating.

Photo 7: Structural framework.

Photo 8: White zirconia framework, 1125 MPa (KATANA HT).

Once the structural file is generated, it is called up within the modeling software to create the anatomical components that will be divided into quadrants.

Photo 9: File divided into three seqments.

The selected material is multi-layered KATANA™ Zirconia STML by Kuraray Noritake Dental Inc. with a flexural strength of 750 MPa and high translucency. KATANA™ Zirconia STML shows an optimized balance between mechanical and optical characteristics.

The author's choice to divide the anatomical components into three segments has a dual purpose: the first is to have a better quality of the milling and the second is to reduce the material waste of the zirconia disc as much as possible.

Photo 10: The three segments after sintering.

Once the frameworks are obtained, before they are merged with each other, the anatomical parts are finished and polished; only the areas excluded from the functional part will be sandblasted. Special attention must be paid to the surface texturing of the anterior sectors⁵, with cutters, discs and rubbers dedicated for this purpose. The surfaces that remain shiny offer a lower abrasion coefficient than the natural tooth⁶; in fact, the abrasiveness depends on the surface smoothing. Polished zirconia has lower abrasion coefficients than lithium disilicate and layered ceramics⁷.

The adhesion between the anatomical and structural zirconia components is achieved by fusion with Noritake Cerabien ZR Low Fusion ceramic.

Photo 11: Anatomical components joined to the structural framework.

Once the adhesion between the zirconia components has been obtained, the first analog phase involves the creation of the gum parts, with dedicated pink gingival masses at a high temperature of 940 C° (CZR™ Tissue Kuraray Noritake Dental Inc.). The author selects three gingival masses with which the keratinized and vascularised parts are reproduced8, peculiar to the natural gingival tissue.

Photo 12: Used CZR™ Tissue porcelain.

Photo 13: Application of CZR™ Tissue porcelain.

Once the pink gingival parts are finalized, the coloring of the anatomical components will follow with the use of dedicated low temperature stains (CZR™ FC Paste Stain, Kuraray Noritake Dental Inc.) which, together with the high translucency of the anatomical zirconia, guarantees a high aesthetic result.

With gray, blue and black shades, it is possible to give a high degree of translucency to the incisal edges. With warm shades, like orange and yellow, the transitions of the anatomical crowns are emphasized, while with a few spots of strong color it is possible to give character and uniqueness to the teeth.

Photo 14: Used shades of CZR™ FC Paste Stain.

The low baking temperature of CZR™ FC Paste Stain guarantees the non-alteration of the gingival component. The final step involves glazing the sandblasted parts.

Photo 15: Final situation.

Photo 16: Occlusal view.

CONCLUSION

The strength of dento-skeletal rehabilitations made of monolithic zirconia, which is a stable, reliable and highly biocompatible material is, through the possibility of using CAD/CAM technology to make an exact copy of a case or, even better, a functionalized temporary implant.

Photo 17: Matching with wax-up.

The 1125 MPa zirconia is ideal for this type of prosthesis, however, does not offer an aesthetic quality. Therefore, the combination of two zirconia materials, one extremely strong and the other highly aesthetic, fully satisfies this requirement.

Photo 18, 19: Intra-oral situation.

BIBLIOGRAPHY:

1) Matteo Chiapasco, Eugenio Romeo La riabilitazione implantoprotesica nei casi compless, UTET S.p.A. 2003 Unione Tipografico-Editrice Torinese.

2) Piconi C. ,Rimondini L. ,Cerroni L. , La zirconia in odontoiatria, Masson, 2008.

3) Stawarczyk B., Ozcan M., Hallmann L., Ender A., Mehl A., Hammerle CH., Effect of zirconia sintering temperature on flexural strengh, grain size and contrast ratio. Clin oral investig, 2013.

5) Shigeo Kataoka, Yoshimi Nishimura , Morfologia naturale dei denti, Edizione internazionale Milano 2003
La riabilitazione implantoprotesica nei casi compless.

6) Oh W., Delong R., Anusavice K., Factors affecting enamel and ceramic wear: A literature review. J Prosthet Dent 2002.

7) Preis V., Bher M., Kolbeck C., Hahnel S., Handel G., Rosentritt M., Wear performance of substructure ceramics and veneering porcelains, Dent Mater, 2011.

8) Rutten L. & P., L’estetica su impianti, editrice MEA, 1999.

Thanks: Dr. Fortunato Alfonsi, Odt. Raoul Pietropaolo.

By Marco Stoppaccioli

In today´s society, due to higher life expectancy, greater and more responsible attention to one´s body, we have developed a culture more sensitive to personal well-being. Consequently, more patients with total removable prostheses request stabilization of their prostheses through implant treatment which offers the most effective and valid response to this need.

The demand for implant treatments has increased significantly during the last decade, specifically from patients with long-term full prostheses resulting in considerable bone resorption¹, but are hesitant to undergo complex bone regeneration interventions (Photo 1).

These rehabilitations require great commitment and professional skills. In addition to restoring a complex series of aesthetic-functional parameters that have been lost. Innovative products were developed, not only the restoration of the dental, but also, the orthopedic aspects of the procedure.

Photo 1: Upper and lower Jaw situation models.

Initially, the dental-skeletal rehabilitations involved the exclusive use of metal posts combined with acrylic materials.

In recent decades, we have witnessed an evolution in the surgical techniques and materials used, among these, zirconia² has a significant and highly innovative role. The main reason for its success is due to the possibility of being able to use it anatomically through a simple and effective protocol thanks to CAD CAM technology.

Zirconia, created to be covered with ceramic coatings, has undergone a profound evolution: from an exclusively structural material with high strength but low aesthetic appeal, it has become anatomical, constituting an alternative to layered restorations. Thanks to research and innovation, optimizing chemical and physical parameters³ in the dental industry, we now have a wide range of products, including multi-layer zirconia.

In more analytical terms, it offers a very valid response to the translucency, which is inversely proportional to the flexural strength. On the market this material class oscillates between 550Mpa and 1200Mpa of flexural strength. This characteristic identifies its indication range, specifically depending on the yttrium oxide content, which acts as a stabilizer of zirconia.

For dental-skeletal rehabilitations, the protocol involves the use of multi-layer monolithic zirconia with marked characteristics of flexural strength but lower translucency which determines a limit in the aesthetic sense. On the other hand, the use of multi-layered zirconia with high translucency cannot be considered suitable, due to its lack of flexural strength, despite fully meeting the requirement for naturalness.

To date it can be said that there is no zirconia that offers high mechanical properties combined with high translucency, two fundamental aspects for successful restorations.

Considering these factors, the idea was born to generate an innovative and experimental protocol capable of supporting, on the one hand, the ability of CAD/CAM systems to copy exactly a project or even better, a functionalized provisional implant, and on the other, to associate the use of two zirconia with different characteristics: one extremely tough, white colored zirconia with 1125 MPa (KATANA™ HT Kuraray Noritake) and the other super translucent multi-layered zirconia with 750 MPa (KATANA™ STML Kuraray Noritake).

OPERATIONAL PROTOCOL

In dental-skeletal rehabilitations, success depends on a precise diagnosis by the clinician, aimed at the functional and aesthetic restoration of the case. It is a fundamental task of the dental technician to translate this information through the creation of a wax-up, both analog and digital.

Photo 2: Digital wax-up.

Photo 3: Analog wax-up.

Thanks to digitization, with a 3D printer, it is possible to realize the wax-up quickly and economically in a prototype, capable of allowing the clinician to perform an initial test in the oral cavity.

Photo 4: From design to 3D prototype.

Once the adequacy of the prototype under study has been certified, the next phase involves the construction of the provisional implant which, placed in the oral cavity for a specified time, provides the fundamental information from an occlusal point of view, both in static and dynamic conditions.

The first strength of this protocol is to capture all information about the provisional implant and transfer them to the final work through digital systems. In other words, the provisional implant itself becomes the design of the final product.

Photo 5: Temporary result of analog project.

Photo 6: Acquisition of temporary arches refitted on the models.

FINAL PROCEDURE: OPERATING PHASES

Once the scans of the temporary implant have been acquired in the digital platform, the structural frame obtained by reduction of the temporary implant file is generated. The framework will be made by using KATANA™ HT white colored zirconia (Kuraray Noritake Dental Inc.) with a flexural strength of 1125 MPa. This choice is attributable to an adequate toughness of the material and an effective aesthetic chromatic response on the pink ceramic coating.

Photo 7: Structural framework.

Photo 8: White zirconia framework, 1125 MPa (KATANA HT).

Once the structural file is generated, it is called up within the modeling software to create the anatomical components that will be divided into quadrants.

Photo 9: File divided into three seqments.

The selected material is multi-layered KATANA™ Zirconia STML by Kuraray Noritake Dental Inc. with a flexural strength of 750 MPa and high translucency. KATANA™ Zirconia STML shows an optimized balance between mechanical and optical characteristics.

The author's choice to divide the anatomical components into three segments has a dual purpose: the first is to have a better quality of the milling and the second is to reduce the material waste of the zirconia disc as much as possible.

Photo 10: The three segments after sintering.

Once the frameworks are obtained, before they are merged with each other, the anatomical parts are finished and polished; only the areas excluded from the functional part will be sandblasted. Special attention must be paid to the surface texturing of the anterior sectors⁵, with cutters, discs and rubbers dedicated for this purpose. The surfaces that remain shiny offer a lower abrasion coefficient than the natural tooth⁶; in fact, the abrasiveness depends on the surface smoothing. Polished zirconia has lower abrasion coefficients than lithium disilicate and layered ceramics⁷.

The adhesion between the anatomical and structural zirconia components is achieved by fusion with Noritake Cerabien ZR Low Fusion ceramic.

Photo 11: Anatomical components joined to the structural framework.

Once the adhesion between the zirconia components has been obtained, the first analog phase involves the creation of the gum parts, with dedicated pink gingival masses at a high temperature of 940 C° (CZR™ Tissue Kuraray Noritake Dental Inc.). The author selects three gingival masses with which the keratinized and vascularised parts are reproduced8, peculiar to the natural gingival tissue.

Photo 12: Used CZR™ Tissue porcelain.

Photo 13: Application of CZR™ Tissue porcelain.

Once the pink gingival parts are finalized, the coloring of the anatomical components will follow with the use of dedicated low temperature stains (CZR™ FC Paste Stain, Kuraray Noritake Dental Inc.) which, together with the high translucency of the anatomical zirconia, guarantees a high aesthetic result.

With gray, blue and black shades, it is possible to give a high degree of translucency to the incisal edges. With warm shades, like orange and yellow, the transitions of the anatomical crowns are emphasized, while with a few spots of strong color it is possible to give character and uniqueness to the teeth.

Photo 14: Used shades of CZR™ FC Paste Stain.

The low baking temperature of CZR™ FC Paste Stain guarantees the non-alteration of the gingival component. The final step involves glazing the sandblasted parts.

Photo 15: Final situation.

Photo 16: Occlusal view.

CONCLUSION

The strength of dento-skeletal rehabilitations made of monolithic zirconia, which is a stable, reliable and highly biocompatible material is, through the possibility of using CAD/CAM technology to make an exact copy of a case or, even better, a functionalized temporary implant.

Photo 17: Matching with wax-up.

The 1125 MPa zirconia is ideal for this type of prosthesis, however, does not offer an aesthetic quality. Therefore, the combination of two zirconia materials, one extremely strong and the other highly aesthetic, fully satisfies this requirement.

Photo 18, 19: Intra-oral situation.

BIBLIOGRAPHY:

1) Matteo Chiapasco, Eugenio Romeo La riabilitazione implantoprotesica nei casi compless, UTET S.p.A. 2003 Unione Tipografico-Editrice Torinese.

2) Piconi C. ,Rimondini L. ,Cerroni L. , La zirconia in odontoiatria, Masson, 2008.

3) Stawarczyk B., Ozcan M., Hallmann L., Ender A., Mehl A., Hammerle CH., Effect of zirconia sintering temperature on flexural strengh, grain size and contrast ratio. Clin oral investig, 2013.

5) Shigeo Kataoka, Yoshimi Nishimura , Morfologia naturale dei denti, Edizione internazionale Milano 2003
La riabilitazione implantoprotesica nei casi compless.

6) Oh W., Delong R., Anusavice K., Factors affecting enamel and ceramic wear: A literature review. J Prosthet Dent 2002.

7) Preis V., Bher M., Kolbeck C., Hahnel S., Handel G., Rosentritt M., Wear performance of substructure ceramics and veneering porcelains, Dent Mater, 2011.

8) Rutten L. & P., L’estetica su impianti, editrice MEA, 1999.

Thanks: Dr. Fortunato Alfonsi, Odt. Raoul Pietropaolo.